PA6(尼龍6)BG30X/德國朗盛/物性表參數(shù)

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.48
	Molding shrinkage, transverse	60x60x2; 280 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.77
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.12
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.16
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	6300	3100
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	125	65
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	4.0	10
	Tensile creep modulus	1 h	MPa	ISO 899-1		2400
	Tensile creep modulus	1000 h	MPa	ISO 899-1		2000
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	45	75
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	40	45
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	< 10	10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Charpy notched impact strength	-40 °C	kJ/m²	ISO 179-1eA	< 10	< 10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	35	60
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	30	40
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Izod notched impact strength	-40 °C	kJ/m²	ISO 180-1A	< 10	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	5800	2800
	Flexural strength	2 mm/min	MPa	ISO 178-A	185	100
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	5.0	8.0
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	170	80
	Puncture maximum force	23 °C	N	ISO 6603-2	700
	Puncture maximum force	-30 °C	N	ISO 6603-2	690
	Puncture energy	23 °C	J	ISO 6603-2	2.0
	Puncture energy	-30 °C	J	ISO 6603-2	1.7
	Ball indentation hardness		N/mm²	ISO 2039-1	185	75
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	190
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	210
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	> 200
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Burning behavior UL 94	1.5 mm	Class	UL 94	HB
	Burning behavior UL 94	0.75 mm	Class	UL 94	HB
	Oxygen index	Method A	%	ISO 4589-2	23
	Glow wire test (GWFI)	2.0 mm	°C	IEC 60695-2-12	650
	Burning behavior US-FMVSS302			ISO 3795	passed
	Vicat softening temperature	50 N; 50 °C/h	°C	ISO 306	> 200
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.5	16
	Relative permittivity	1 MHz	-	IEC 60250	4.0	4.8
	Dissipation factor	100 Hz	10-4	IEC 60250	130	3100
	Dissipation factor	1 MHz	10-4	IEC 60250	180	1000
	Volume resistivity		Ohm·m	IEC 60093	1E13	1E09
	Surface resistivity		Ohm	IEC 60093	1E14	1E12
	Electric strength	1 mm	kV/mm	IEC 60243-1	36	30
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	400
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	7
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	2.2
	Density		kg/m³	ISO 1183	1350
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	280
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.12
	Melt temperature (Tmin - Tmax)		°C	-	270-290
	Mold temperature		°C	-	80-120

溫馨提示：
本物性表參數(shù)提供者不承擔(dān)任何法律責(zé)任，建議在選擇材料前，就數(shù)據(jù)值與塑膠材料廠商進(jìn)行驗證。版權(quán)歸原作者所有，如有侵權(quán)請立即與我們聯(lián)系.

上一頁：PA6(尼龍6)BG30FN05/德國朗盛/物性表參數(shù) 下一頁：PA6(尼龍6)BG30XF30/德國朗盛/物性表參數(shù)

返回首頁返回物性參數(shù)列表

PA6(尼龍6)BG30X/德國朗盛/物性表參數(shù)

熱門文章

推薦文章