VALOX(沙伯基礎)4012G/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的VALOX 4012G PBT是一種加10%玻璃纖維增強PBT注塑樹脂，具有優異的機械性能,應用程序:連接器,該等級為4012，具有更好的循環時間和延展性。
 |
沙伯基礎創新塑料的VALOX 4012G PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)4012G/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 80 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 4400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3800 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 80 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 120 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 5 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3800 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 110 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 33 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 33 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 380 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 4 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 6 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 4.63E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 8.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 6.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 4.79E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 2.11E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 205 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 170 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 185 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.35 | - | ASTM D 792 | |
| Filler Content | 10 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.6-1.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.7-1 | % | SABIC method | |
| Melt Flow Rate, 250°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 266°C/5.0 kgf | 90 | g/10 min | ASTM D 1238 | |
| Density | 1.35 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/1.2 kg | 9 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 80 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 110 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.015 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.4 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 150 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 2.0 mm | 775 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 | |
| Injection Molding | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250-270 | °C | ||
| Nozzle Temperature | 240-260 | °C | ||
| Front - Zone 3 Temperature | 245-265 | °C | ||
| Middle - Zone 2 Temperature | 240-255 | °C | ||
| Rear - Zone 1 Temperature | 230-245 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 40-100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：12786 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：11108 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：10762 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9140 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7933 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7903 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7327 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6839 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6532 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6478 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6447 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6344 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：6159 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：6142 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力于其性能的提高和
瀏覽量：6036
推薦文章
-
PA6(尼龍6)8231GHS|BASF(巴斯夫)物性表參數
巴斯夫ULTRAMID P66 8231GHS尼龍樹脂顏色是多種色號、巴斯夫尼龍已為基礎的聚酰胺成型化合物。由于它們良好的性質 ，這些材料已經成為幾乎所有工程領域中的多種部件和機器零件（
-
LCP(工業化液晶聚合物)HA475|寶理塑料|物性表參數
日本寶理LAPEROS LCP HA475 是一種加30%纖維增強,SMT對應, 低翹曲性,低異向性,超高流動性液晶高分子,是我們從傳統的塑料所想象不到的，具有非常特別的結構和性能的高分子，取Themotropic
-
TPEE/HTR8139/TPEE物性表參數
TPC-ET 物性TPEE 物性參數Hytrel HTR8139 物性表 TPEE HTR8139是美國DuPont杜邦公司熱塑性聚酯彈性體TPEE,商品名Hytrel,兼 有橡膠的彈性工程塑料的強度 ,具有優異的動態力學屬性,優異的耐沖擊性,優
-
PC/AK3020/PC物性表參數
日本出光TARFLON PC AK3020 是一種無溴阻燃1.00mmV-0阻燃等級的PC聚碳酸酯,廣泛用于打印機和復印機零部件、液晶投影儀零部件、接線端子、繼電器外殼、連接器、模塊插頭、燈箱、LED燈、蓄
-
AMILAN(共聚尼龍)CM6241M|TORAY(東麗)物性表參數
TORAY(東麗)Nylon樹脂 AMILAN CM6241M 是一種未增強，柔軟級別的共聚尼龍原料，拉伸強度在23℃測試條件是65MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需求和應用提
-
POM(聚甲醛共聚物)GF705/可隆(KOLON)物性表參數
可隆(KOLON)Kocetal POM GF705是一種加25%玻璃纖維增強聚甲醛共聚物，比重是1.59g/cm3，熔流率(熔體流動速率)(190°C/2.16kg)10.0g/10min，應用于汽車工業 制造汽車泵、汽化器部件、輸油管、動力閥、萬向節軸承、馬達齒輪、曲軸、把手、儀表板、汽車窗升降機裝置、電開關、安全帶扣等。以下是POM(聚甲醛共聚物)GF705/可
-
PBT(聚對苯二甲酸丁二酯)315NF|寶理塑料|物性表參數
日本寶理DURANEX PBT 315NF 是一種加玻纖15%, 非鹵素阻燃劑使用, 高電弧性的聚酯聚合物,由于它具有高的熔點和結晶度，由于其吸水率和線性熱膨脹系數很低，因此具有優良的尺寸穩定性。
-
POK(脂肪族聚酮)M640A|曉星(POKETONE)物性表參數
曉星(POKETONE)POK M640A是一種食品包裝用,低熔點注塑成型脂肪族聚酮樹脂，是能夠使用于汽車燃油輸送管路、內外部裝修材料、電子電器部件、氣體阻隔包裝材料、管子等多種用途的ENPLA材料。以下是POK(脂肪族聚酮)M640A|曉星(POKETONE)物性表參數基本信息特性耐熱性，高、粘度，高外觀自然色加工方法注射成型物理性能額定值單
-
Bayblend(拜本蘭)FR3010IF|科思創(PC/ABS合金)物性表參數
科思創Bayblend PC/ABS FR3010IF 是加阻燃,;維卡軟化點溫度/ B 120 = 108C;耐熱性增加;UL認可94 5VB (1.5 mm);灼熱絲溫度(GWFI):在2.0毫米960C. PC/ABS是聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，
-
PPS(聚苯硫醚)1140A64|寶理塑料|物性表參數
日本寶理 PPS DURAFIDE 1140A64 是一種GF增強 ,標準, 低溢的聚苯硫醚,其用途不僅限于電子零件。可應用于燈座、水泵、各種電裝部件等，作為汽車部件、OA設備、AV設備的功能部件的材料也可