VALOX(沙伯基礎)735/PBT熱塑性聚酯/物性表參數(shù)
沙伯基礎創(chuàng)新塑料SABIC的VALOX 735 PBT是一種加40%玻璃/礦物，優(yōu)異的熱工性能/低收縮,電動加熱設備，適配器環(huán)，烤箱烤架等,提供黑色/自然色。
 |
沙伯基礎創(chuàng)新塑料的VALOX 735 PBT物性表參數(shù)PDF文檔下載 |
以下是VALOX(沙伯基礎)735/PBT熱塑性聚酯/物性表參數(shù)
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8300 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 64 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 2 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 144 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 124 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 40 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 520 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 55 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| Thermal Conductivity | 0.36 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.28E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.53E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.18E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.4E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.62 | - | ASTM D 792 | |
| Filler Content | 40 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
| Density | 1.62 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.96 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 1 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 3 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 15 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 160 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.008 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.017 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.5 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.81 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260 - 285 | °C | ||
| Nozzle Temperature | 265 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 255 - 280 | °C | ||
| Rear - Zone 1 Temperature | 240 - 260 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 110 | °C |
溫馨提示：
本物性表參數(shù)提供者不承擔任何法律責任，建議在選擇材料前，就數(shù)據(jù)值與塑膠材料廠商進行驗證。版權(quán)歸原作者所有，如有侵權(quán)請立即與我們聯(lián)系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數(shù)臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數(shù)位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質(zhì)，可應用於汽車零件、3C電子產(chǎn)品外殼、消費性
瀏覽量：12794 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數(shù)臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質(zhì)，可應用於汽車零件、3C電子產(chǎn)品外殼、消費性電子元件、家電外殼、玩具、板材等產(chǎn)品上，其應用端多元化，本廠設有
瀏覽量：11118 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優(yōu)良的韌性、水解穩(wěn)定性、耐熱性和耐化
瀏覽量：10767 -
ABS塑料樹脂/PA-757/奇美實業(yè)/物性表參數(shù)奇美實業(yè)POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數(shù)是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9143 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉(zhuǎn)換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優(yōu)良的光學性能、良好的可加工性和優(yōu)良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產(chǎn)品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數(shù)PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7941 -
PC(聚碳酸酯)FR6005/科思創(chuàng)(Makrolon)物性表···科思創(chuàng)(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數(shù)MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產(chǎn)品。 以下是PC(聚碳酸
瀏覽量：7906 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7334 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數(shù)···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內(nèi)飾用品等
瀏覽量：6842 -
Bayblend(拜本蘭)FR3010|科思創(chuàng)(PC/ABS合金···科思創(chuàng)Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6536 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數(shù)科思德塑膠網(wǎng)站提供瑞士EMS化學PA12 TR90的物性表參數(shù)下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6483 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規(guī)高結(jié)晶度的特點，這一產(chǎn)品的結(jié)晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產(chǎn)品和高強度汽車部件上使用，這些部件需要在高溫環(huán)境下長期暴露.其特點是：高強度、超高耐熱、高結(jié)晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6451 -
Makrolon(模克隆)2407(科思創(chuàng))PC(聚碳酸酯)···科思創(chuàng)Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數(shù)19 厘米 3 /10分鐘; 普通用途; 紫外線穩(wěn)定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6344 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩(wěn)定性，耐熱性
瀏覽量：6161 -
PC/ABS(PC+ABS合金)PC-540|奇美實業(yè)|物性表···奇美實業(yè)WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數(shù)是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數(shù)碼產(chǎn)品、變壓器、電視游樂器、小平板計算機、網(wǎng)通產(chǎn)品,為了增加PC在薄肉產(chǎn)品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：6146 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數(shù)嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現(xiàn)工業(yè)化生產(chǎn)的聚碳酸酯樹脂，長期以來，帝人一直致力于其性能的提高和
瀏覽量：6042
推薦文章
-
PC(聚碳酸酯)NH3022S/Samyang(三養(yǎng))物性表參數(shù)
Samyang(三養(yǎng))TRIREX PCNH3022S是一種非強化,耐氣候聚碳酸酯，比重是1.21g/cm3，熔流率（熔體流動速率）(300°C/1.2 kg)39g/10min，有著優(yōu)異的機械特性，很好的尺寸穩(wěn)定性及良好的電氣特性，應用于TV,電子電器。以下是PC(聚碳酸酯)NH3022S/Samyang(三養(yǎng))物性表參數(shù)PROPERTYUNITASTM METHODTYPICAL DATAPhysicalSpeci
-
PA6(尼龍6)8231GHS|BASF(巴斯夫)物性表參數(shù)
巴斯夫ULTRAMID P66 8231GHS尼龍樹脂顏色是多種色號、巴斯夫尼龍已為基礎的聚酰胺成型化合物。由于它們良好的性質(zhì) ，這些材料已經(jīng)成為幾乎所有工程領域中的多種部件和機器零件（
-
TPE(熱塑性彈性體)TF7WKF/凱柏膠寶/物性表參數(shù)
凱柏膠寶KRAIBURG熱塑寶K TPE TF7WKF 是一款自然色, 硬度72A,在飲用水系統(tǒng)中的應用,DW系列TPE熱塑性彈性體,典型應用是密封件,衛(wèi)生行業(yè)的功能和設計要素,淋浴頭,材料優(yōu)勢是PP/PE包膠性能,彈性
-
PA66(尼龍66)A3WGM33|BASF(巴斯夫)物性表參數(shù)
巴斯夫ULTRAMID PA66 A3WGM33 是結(jié)合玻璃纖維和礦物增強注塑成型等級，適用于高剛度、尺寸好的零件,穩(wěn)定性和表面光潔度，如汽車氣缸蓋，巴斯夫尼龍是以聚酰胺為基礎的聚酰胺成型
-
PEI/2300/PEI物性表數(shù)據(jù)
PEI2300美國沙伯基礎創(chuàng)新塑料 物性表數(shù)據(jù) 暫無此原料描述部分 ┄ 性能項目 試驗條件[狀態(tài)] 測試方法 測試數(shù)據(jù) 數(shù)據(jù)單位 基本性能 吸水率 24小時，73?H ASTM D-570 0.210 % 吸水率 平衡,73?
-
PC(聚碳酸酯)LUX7432C/沙伯基礎(SABIC)物性表參數(shù)
SABIC(沙伯基礎創(chuàng)新塑料)LEXAN PC LUX7432C 是一種非填充，注塑成型等級,也是無氯化、無溴化阻燃劑PC,具有UL-94 V0等級為1.2 mm / 5VA等級為3.0mm，并具有UV穩(wěn)定(F1等級)的額外抗老化能力LEXAN LUX
-
VYDYNE(泛達)美國奧升德66B|PA66(尼龍66)物性表參數(shù)
美國奧升德VYDYNE PA66 66B 是一種無增強擠出級PA66樹脂。可在自然顏色，它提供了高強度，剛性和韌性的要求廣泛的應用要求。Vydyne擠出級樹脂具有良好的耐多種化學品，機械和電機油，
-
ABS塑料樹脂/PA-726M/奇美實業(yè)/物性表參數(shù)
奇美實業(yè)POLYLAC ABS PA-726M 是電鍍級ABS樹脂,熔融指數(shù)是4g/10min,用途是汽車水箱前欄、汽車飾條 、汽車銘牌 、汽車部件,奇美的POLYLACABS樹脂是現(xiàn)今市場上最多樣化的丙烯腈一丁二烯一苯乙烯
-
TPE(熱塑性彈性體)TC9GPN/凱柏膠寶/物性表參數(shù)
凱柏膠寶KRAIBURG熱塑寶K TPE TC9GPN 是一款自然色, 硬度89A的GP/FG系列TPE材料,用于多種不同應用的材料解決方案,特別適用于客艙,該化合物擁有淡褐色或黑色可供選擇，典型應用：功能和設計
-
塞拉尼斯TPV 253-50W232|Santoprene物性表參數(shù)
Celanese(塞拉尼斯)SANTOPRENE(山都坪)TPV 253-50W232是一種熱塑性硫化彈性體，它也是一種堅硬、可著色的熱塑性硫化膠(TPV)，這種材料具有良好的流體阻力，并被配制成替代熱固性橡膠，如三元乙丙橡膠，聚氯丁橡膠和氯磺化聚乙烯，該等級的Santoprene TPV是剪切依賴的，可以在傳統(tǒng)的熱塑性塑料設備上進行注射成型，擠出或吹塑