VALOX(沙伯基礎)DR51/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的VALOX DR51 PBT是一種加15% GR聚酯，優異的機械、熱和電氣性能。無焰阻燃,射燈，電器外殼，把手，連接器。
 |
沙伯基礎創新塑料的VALOX DR51 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)DR51/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 90 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 90 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 5900 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 140 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 140 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4500 | MPa | ASTM D 790 | |
| Hardness, Rockwell R | 118 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 95 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 5 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5100 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 100 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 30 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 27 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 330 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 330 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 40 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 40 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -20°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 4 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 4 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 4 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, annealed | 193 | °C | ASTM D 648 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 190 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.16E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.58E-05 | 1/°C | ASTM E 831 | |
| CTE, 60°C to 138°C, flow | 2.16E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 3.35E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.06E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 3.4E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.83E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 210 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 205 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.45 | - | ASTM D 792 | |
| Specific Volume | 0.71 | cm³/g | ASTM D 792 | |
| Filler Content | 17 | % | ASTM D 229 | |
| Water Absorption, 24 hours | 0.07 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 1.5-3.2 mm | 0.4-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2-4.6 mm | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 0.8-1.1 | % | SABIC method | |
| Melt Flow Rate, 265°C/5.0 kgf | 80 | g/10 min | ASTM D 1238 | |
| Density | 1.45 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Flow Rate, 250°C/2.16 kg | 18 | g/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 15 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 43 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 65 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 170 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 19.6 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23.2 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3.4 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 | |
| Comparative Tracking Index | 300 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.75 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：12785 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：11107 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：10761 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9138 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7932 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7902 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7326 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6838 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6531 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6477 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6446 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6343 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：6158 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：6141 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力于其性能的提高和
瀏覽量：6035
推薦文章
-
TPU(熱塑性聚氨酯彈性體)6080A/科思創/物性表參數
科思創(Covestro)的Desmopan(德士模班) TPU 6080A 是熱塑性聚氨酯彈性體，邵氏硬度80A(DIN ISO 7619-1)，注塑級，從增塑劑自由;簡單的流動;具有良好的水解和微生物抗性;低磨損, 耐氣候，抗磨損
-
PA66(尼龍66)AKV25H3.0LT/德國朗盛/物性表參數
德國朗盛 Durethan PA66 AKV25H3.0LT 是一種p66, 25%玻璃纖維，注塑，熱老化穩定，nir -激光透明著色(黑色)尼龍樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑
-
PP(聚丙烯)RP548N/利安德巴塞爾/物性表參數
利安德巴塞爾(Lyondellbasell)Pro-fax PP RP548N是一種成核聚丙烯無規共聚物以顆粒形式提供，熔體流動速率(230°C/2.16kg)是11克/10分鐘，密度(23°C)是0.898克/厘米3，這種樹脂通常用于注塑成型應用，并提供快速結晶和抗靜電性能。以下是PP(聚丙烯)RP548N/利安德巴塞爾/物性表參數基本信息添加劑成核劑特性成核的抗靜電
-
RYTON(索爾維)R-4-220NA|PPS(聚苯硫醚)物性表參數
SOLVAY(索爾維)Ryton PPS R-4-220NA 是一款添加40%玻璃纖維，自然色聚苯硫醚原料，特性是更高的強度和韌性，材料優勢是可精密成型、阻燃、良好的電氣性能、熱固性樹脂替代材料、耐熱沖擊
-
POM(聚甲醛共聚物)UV140LG/塞拉尼斯(CELANESE)物性表參數
塞拉尼斯(CELANESE)Celcon POM UV140LG是一種抗UV低光澤聚甲醛共聚物，密度是1.33g/cm3，溶化體積流率（MVR）(190°C/2.16 kg)是13.0cm3/10min，為汽車內飾應用提供良好的流動性和低光澤度和紫外線穩定性。以下是POM(聚甲醛共聚物)UV140LG/塞拉尼斯(CELANESE)物性表參數基本信息添加劑紫外線穩定劑特性光澤，低良好的
-
POM(聚甲醛)F20-03/三菱塑料/物性表參數
日本三菱Iupital POM F20-03是一種聚甲醛（POM）共聚物，密度是1.41g/cm，熔流率（熔體流動速率）(190C/2.16 kg) 9.0g/10 min，拉伸模量是2900MPa，F20-03的典型應用領域為:汽車行業。 以上是POM(聚甲醛
-
PC(聚碳酸酯)DQ5162/科思創(Makrolon)物性表參數
科思創(Covestro)模克隆(Makrolon) PC DQ5162 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 34cm cm /10 min，光擴散等級;高光擴散;低粘度;紫外線穩定，含有脫模劑，適用于LED產品。 以下是PC
-
PPA(聚鄰苯二甲酰胺)GV XE 16101|艾曼斯|物性表參數
艾曼斯Grivory PPA GV XE 16101材料是一種Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X)材料,含有的填充物為40% 玻璃纖維增強材料。 該產品在北美洲、非洲和中東、拉丁美洲、歐洲或亞太地區有供貨
-
LEXAN(沙伯基礎）943X/PC聚碳酸酯/物性表參數
SABIC沙伯基礎創新塑料Copolymer系列 LEXAN PC 943X 是一種紫外線穩定介質流動沖擊改性注射成型(IM)等級。該樹脂以非溴、非氯FR系統、低溫延性特性和極好的加工能力為基礎，提供了UL94 V0
-
POM(聚甲醛樹脂)SW-41/日本寶理/物性表參數
日本寶理奪鋼DURACON POM SW-41 是一種高剛性,高耐沖擊,高滑動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu