LEXAN(沙伯基礎)505R/PC(聚碳酸酯)物性表參數
沙伯基礎SABIC塑料LEXAN 505R聚碳酸酯（PC）是一種可注射成型的非氯化和非溴化阻燃級，填充10％玻璃纖維, 它具有UL94 V0@1.5mm的額定值，并提供各種不透明顏色選項, 這是LEXAN 500,500R，500RS，500ECR的替代品。
 |
沙伯基礎SABIC塑料LEXAN 505R PC物性表參數PDF文檔下載 |
以下是LEXAN(沙伯基礎)505R/PC(聚碳酸酯)物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 63 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 12 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3930 | MPa | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 108 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3530 | MPa | ASTM D 790 | |
| Hardness, Rockwell M | 85 | - | ASTM D 785 | |
| Hardness, Rockwell R | 124 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 11 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3400 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 115 | MPa | ISO 2039-1 | |
| IMPACT | ||||
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 107 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 61 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | 130 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m² | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 15 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Specific Heat | 1.21 | J/g-°C | ASTM C 351 | |
| Thermal Conductivity | 0.2 | W/m-°C | ASTM C177 | |
| Vicat Softening Temp, Rate B/50 | 149 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 143 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.68E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.46E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.21 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 80°C, flow | 4.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 141 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 144 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Ae | |
| HDT/Ae, 1.8 MPa Annealed 120°C, 2hrs | 136 | °C | ISO 75/Ae | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Af | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Bf | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.26 | - | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 | |
| Water Absorption, 24 hours | 0.12 | % | ASTM D 570 | |
| Water Absorption, equilibrium, 23C | 0.31 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 7 | g/10 min | ASTM D 1238 | |
| Density | 1.25 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.31 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm³/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 33 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94-5VA Flame Class Rating | 3 | mm | UL 94 | |
| UL Compliant, 94-5VB Rating | 2 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Oxygen Index (LOI) | 37 | % | ISO 4589 | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 290-320 | °C | ||
| Nozzle Temperature | 280-310 | °C | ||
| Front - Zone 3 Temperature | 290-320 | °C | ||
| Middle - Zone 2 Temperature | 280-310 | °C | ||
| Rear - Zone 1 Temperature | 270-300 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 80-120 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺化/物性表參數臺化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用于筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：12779 -
PC/ABS(PC+ABS合金)AC2300/臺化/物性表參數臺化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用于汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高沖擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：11099 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基于脫模來源于蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：10755 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、復印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9135 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7929 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級，透明高光澤，適用于電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：7901 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7326 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方面的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、復印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6833 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6528 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6473 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助于在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表面硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6446 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鐘; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6342 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對于伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：6157 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視游樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐沖擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐沖擊性之新材料,一般用于計算機外殼及
瀏覽量：6139 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力于其性能的提高和
瀏覽量：6033
推薦文章
-
PC(聚碳酸酯)R9453/沙伯基礎(SABIC)物性表參數
沙伯基礎(SABIC)LEXAN PC R9453是一種非填充、無氯、無溴的通用阻燃聚碳酸酯（PC）樹脂，含有30%的消費后再生PC，這種樹脂是UL-94 V0等級和各種注塑應用。以下是PC(聚碳酸酯)R9453/沙伯基礎(SABIC)物性表參數產品特性阻燃無氯無溴含回收料成型方式注塑技術參數物理性能值/單位測試標準測試條件比重1.19 -ASTM D792熔體質量流
-
PBT(聚對苯二甲酸丁二酯)RH1150T01|寶理塑料|物性表參數
日本寶理DURANEX PBT MH6304T01 是一種GF15%增強, 不阻燃,低噪音, 減振的聚酯聚合物,由于它具有高的熔點和結晶度，由于其吸水率和線性熱膨脹系數很低，因此具有優良的尺寸穩定性。此外，
-
PC(聚碳酸酯)GSH2040DF|三菱工程塑料|物性表參數
三菱工程塑料Iupilon/NOVAREX/XANTAR PC GSH2040DF是加40%玻纖復合強化,低翹曲品級,體積熔融指數5.0厘米3/10分鐘; 易脫模; 注塑成型,被廣泛地用于各種工業生產，如運動器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶的廣泛信賴和支持。Iupilon PC GSH2040DF物性表參數PDF文檔下載以下是PC(聚
-
PA66(尼龍66)85XFS|美國奧升德(泛達)物性表參數
美國奧升德VYDYNE PA66 85XFS 是一種通用的PA66/6共聚物樹脂。它是在自然和設計擠出復合應用。該共聚物PA66/6樹脂具有較低的熔點，可用于復合熱敏添加劑或填料。 85XFS是高強度、高剛性、
-
PA6(尼龍6)BG30XH3.0/德國朗盛/物性表參數
德國朗盛 LANXESS Durethan PA6 BG30XH3.0 是一種加30%玻璃/玻璃球，注塑成型，熱老化穩定，易彎曲尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的
-
PA66(尼龍66)EPR27N/神馬(Shenma)物性表參數
神馬(Shenma)PA66EPR27N是一種有光、中等粘度尼龍66，外潤滑，主要用于注塑，有較好的產品流動性。以下是PA66(尼龍66)EPR27N/神馬(Shenma)物性表參數產品特性良好流動性中粘度成型方式注塑技術參數物理性能值/單位測試標準測試條件粘度2.57 -Internalrelative viscosity溫馨提示：本物性表參數提供者不承擔任何法律責
-
PC/ABS(PC合金)LDS3724|三菱工程塑料|物性表參數
三菱工程塑料XANTAR PC/ABS LDS3724是鐳雕級別的聚碳酸酯+ABS合金材料,體積熔融指數14厘米3/10分鐘; 密度是1.23g/cm3，拉伸模量是2250MPa，維卡軟化溫度122°C, 特性是：激光標記 ;磷含量，低（到無） ;無溴阻燃性，被廣泛地用于各種工業生產，如運動器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶
-
PP(聚丙烯)B920G/韓國SK/物性表參數
韓國SK Global Chemical Yuplene PP B920G是一種為注射成形的而研制的抗沖擊聚丙烯，它具有很好的耐沖性和樹脂穩定性，因此已獲得了 UL認證，熔體流動速率(230°C/2.16kg)是2.5克/10分鐘，YUPLENE B920G可用于瓶蓋制造。以下是PP(聚丙烯)B920G/韓國SK/物性表參數項目質量指示單位實驗方法熔融指數2.5g/10minASTM D1238維
-
PEEK(聚醚醚酮)4000G/贏創德固賽/物性表參數
贏創德固賽VESTAKEEP PEEK 4000G是一種高粘度、無增強聚醚醚酮，用于注塑成型和擠壓成型，這種半結晶聚合物具有優異的耐熱性和耐化學性，采用VESTAKEEP 4000G制造的部件具有自熄性，VESTAKEEP 4000G可在普通熱塑性塑料設備上加工，我們建議在注塑過程中熔體溫度在370°C-380°C之間，模具溫度應在160°C ~ 200°C范圍內，保
-
PC（聚碳酸酯）EXL1494T|沙伯基礎|物性表參數
沙伯基礎LEXAN PC EXL1494T聚碳酸酯(PC)硅氧烷共聚物樹脂是注射成型級與FDA和歐盟食品接觸合規，該樹脂具有很低溫(-40℃)延展性，結合介質流動特性，改進的釋放和優異的加工性能，與標準PC相比，IM周期時間更短，LEXAN EXL1494T樹脂可提供透明和不透明的顏色，是廣泛的食品接觸應用的材料。以下是PC（聚碳酸酯）EXL1494T/沙