PC(聚碳酸酯)FXD9810/沙伯基礎(SABIC)物性表參數

日期：2020-06-16 02:44:22 編輯：科思德塑膠來源：科思德塑膠瀏覽：285

SABIC(沙伯基礎創新塑料)LEXAN PC FXD9810是無氯化，無溴化阻燃pc加硅氧烷共聚物共混,優異的加工性能，高流動，良好的沖擊性能，UL等級V-0，有限的半透明的顏色。

以下是PC(聚碳酸酯)FXD9810/沙伯基礎(SABIC)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E207780-592770	-	-
UL Recognized, 94V-0 Flame Class Rating		≥1.2	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating		≥1	mm	UL 94
Glow Wire Ignitability Temperature, 1.2 mm		875	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.0 mm		850	°C	IEC 60695-2-13
Glow Wire Flammability Index, 1.2 mm		930	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.0 mm		875	°C	IEC 60695-2-12
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min		55	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min		50	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min		5.6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min		100	%	ASTM D 638
Tensile Modulus, 50 mm/min		2200	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span		94	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span		2100	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min		56	MPa	ISO 527
Tensile Stress, break, 50 mm/min		49	MPa	ISO 527
Tensile Strain, yield, 50 mm/min		5.6	%	ISO 527
Tensile Strain, break, 50 mm/min		95	%	ISO 527
Tensile Modulus, 1 mm/min		2150	MPa	ISO 527
Flexural Stress, yield, 2 mm/min		91	MPa	ISO 178
Flexural Modulus, 2 mm/min		2250	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C		690	J/m	ASTM D 256
Izod Impact, notched, -30°C		220	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C		63	J	ASTM D 3763
Izod Impact, notched 80104 +23°C		40	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C		19	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm		49	kJ/m²	ISO 179/1eA
THERMAL
Vicat Softening Temp, Rate B/50		136	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed		118	°C	ASTM D 648
CTE, -40°C to 40°C, flow		7.05E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow		7.03E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow		6.9E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow		6.8E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C		Pass	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50		137	°C	ISO 306
Vicat Softening Temp, Rate B/120		138	°C	ISO 306
Relative Temp Index, Elec	¹⁾	120	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	110	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	120	°C	UL 746B
PHYSICAL
Specific Gravity		1.19	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm		0.4-0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm		0.4-0.8	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf		30	g/10 min	ASTM D 1238
Density		1.19	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)		0.26	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)		0.08	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg		29	cm³/10 min	ISO 1133
ELECTRICAL
Comparative Tracking Index (UL) {PLC}		3	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 2		≥1	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2		≥1	mm	UL 746A
Injection Molding
Drying Temperature		120	°C
Drying Time		3-4	hrs
Drying Time (Cumulative)		48	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		270-295	°C
Nozzle Temperature		265-290	°C
Front - Zone 3 Temperature		270-295	°C
Middle - Zone 2 Temperature		260-280	°C
Rear - Zone 1 Temperature		250-270	°C
Mold Temperature		70-95	°C
Back Pressure		0.3-0.7	MPa
Screw Speed		40-70	rpm
Shot to Cylinder Size		40-60	%
Vent Depth		0.025-0.076	mm

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯系.
為及時發現和糾正網站存在的信息內容等方面問題，在使用網站時及時反饋網站問題，從而幫助推進網站信息內容建設工作，提高網站信息互動交流。

上一頁：PC(聚碳酸酯)FXD1414T/沙伯基礎(SABIC)物性表參數下一頁：PC(聚碳酸酯)FXE1112T/沙伯基礎(SABIC)物性表參數

返回首頁返回物性參數列表

PC(聚碳酸酯)FXD9810/沙伯基礎(SABIC)物性表參數

熱門文章

推薦文章