PA66(尼龍66)22G5/長(zhǎng)春化工(漳州)/物性表參數(shù)
以下是PA66(尼龍66)22G5/長(zhǎng)春化工(漳州)/物性表參數(shù)
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 |
3.4 %
@Thickness 2.00 mm
|
3.4 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 |
0.900 %
@Thickness 2.00 mm
|
0.900 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 |
85370 cP
@Shear Rate 5000 1/s, Temperature 280 °C
|
85370 cP
@Shear Rate 5000 1/s, Temperature 536 °F
|
ISO 11403-1 -2 |
|
138900 cP
@Shear Rate 5000 1/s, Temperature 270 °C
|
138900 cP
@Shear Rate 5000 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
|
243400 cP
@Shear Rate 5000 1/s, Temperature 260 °C
|
243400 cP
@Shear Rate 5000 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
|
270750 cP
@Shear Rate 500 1/s, Temperature 280 °C
|
270750 cP
@Shear Rate 500 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
|
441600 cP
@Shear Rate 500 1/s, Temperature 270 °C
|
441600 cP
@Shear Rate 500 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
|
774800 cP
@Shear Rate 500 1/s, Temperature 260 °C
|
774800 cP
@Shear Rate 500 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 粘度測(cè)試 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 線性成型收縮率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 線性成型收縮率，橫向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| 機(jī)械性能 | 額定值 (公制) | 額定值 (英制) | 測(cè)試方法 |
|---|---|---|---|
| 抗張強(qiáng)度(斷裂) | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |
| 抗張強(qiáng)度 |
8.79 MPa
@Strain 0.230 %, Temperature 150 °C
|
1270 psi
@Strain 0.230 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
|
12.0 MPa
@Strain 0.240 %, Temperature 90.0 °C
|
1740 psi
@Strain 0.240 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
15.95 MPa
@Strain 0.470 %, Temperature 150 °C
|
2313 psi
@Strain 0.470 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
22.76 MPa
@Strain 0.480 %, Temperature 90.0 °C
|
3301 psi
@Strain 0.480 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
24.06 MPa
@Strain 0.700 %, Temperature 150 °C
|
3490 psi
@Strain 0.700 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
25.92 MPa
@Strain 0.400 %, Temperature 40.0 °C
|
3759 psi
@Strain 0.400 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
31.12 MPa
@Strain 1.10 %, Temperature 150 °C
|
4514 psi
@Strain 1.10 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
34.25 MPa
@Strain 0.790 %, Temperature 90.0 °C
|
4968 psi
@Strain 0.790 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
37.13 MPa
@Strain 0.540 %, Temperature 40.0 °C
|
5385 psi
@Strain 0.540 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
41.37 MPa
@Strain 0.570 %, Temperature 23.0 °C
|
6000 psi
@Strain 0.570 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
41.5 MPa
@Strain 0.470 %, Temperature 23.0 °C
|
6020 psi
@Strain 0.470 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
42.25 MPa
@Strain 1.55 %, Temperature 150 °C
|
6128 psi
@Strain 1.55 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
44.11 MPa
@Strain 2.01 %, Temperature 150 °C
|
6398 psi
@Strain 2.01 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
44.88 MPa
@Strain 1.15 %, Temperature 90.0 °C
|
6509 psi
@Strain 1.15 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
52.61 MPa
@Strain 3.26 %, Temperature 150 °C
|
7630 psi
@Strain 3.26 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
54.28 MPa
@Strain 0.980 %, Temperature 40.0 °C
|
7873 psi
@Strain 0.980 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
55.02 MPa
@Strain 2.75 %, Temperature 150 °C
|
7980 psi
@Strain 2.75 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
57.51 MPa
@Strain 1.63 %, Temperature 90.0 °C
|
8341 psi
@Strain 1.63 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
63.12 MPa
@Strain 2.08 %, Temperature 90.0 °C
|
9155 psi
@Strain 2.08 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
63.72 MPa
@Strain 0.650 %, Temperature -20.0 °C
|
9242 psi
@Strain 0.650 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
67.98 MPa
@Strain 0.820 %, Temperature 0.000 °C
|
9860 psi
@Strain 0.820 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
71.93 MPa
@Strain 3.50 %, Temperature 90.0 °C
|
10430 psi
@Strain 3.50 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
|
72.3 MPa
@Strain 0.770 %, Temperature 0.000 °C
|
10500 psi
@Strain 0.770 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
|
73.4 MPa
@Strain 1.26 %, Temperature 40.0 °C
|
10600 psi
@Strain 1.26 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
73.91 MPa
@Strain 1.18 %, Temperature 23.0 °C
|
10720 psi
@Strain 1.18 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
74.49 MPa
@Strain 2.80 %, Temperature 90.0 °C
|
10800 psi
@Strain 2.80 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
|
78.89 MPa
@Strain 0.830 %, Temperature -20.0 °C
|
11440 psi
@Strain 0.830 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
|
79.11 MPa
@Strain 1.75 %, Temperature 40.0 °C
|
11470 psi
@Strain 1.75 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
84.04 MPa
@Strain 1.04 %, Temperature 23.0 °C
|
12190 psi
@Strain 1.04 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
94.42 MPa
@Strain 2.82 %, Temperature 40.0 °C
|
13690 psi
@Strain 2.82 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.33 MPa
@Strain 1.96 %, Temperature 23.0 °C
|
14552 psi
@Strain 1.96 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.68 MPa
@Strain 1.34 %, Temperature 0.000 °C
|
14602 psi
@Strain 1.34 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
100.92 MPa
@Strain 2.18 %, Temperature 40.0 °C
|
14637 psi
@Strain 2.18 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
|
101.62 MPa
@Strain 1.11 %, Temperature -20.0 °C
|
14739 psi
@Strain 1.11 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
118.66 MPa
@Strain 1.78 %, Temperature 23.0 °C
|
17210 psi
@Strain 1.78 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
|
120.54 MPa
@Strain 1.46 %, Temperature 0.000 °C
|
17483 psi
@Strain 1.46 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
|
127.28 MPa
@Strain 1.98 %, Temperature 0.000 °C
|
18460 psi
@Strain 1.98 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
|
134.63 MPa
@Strain 1.66 %, Temperature -20.0 °C
|
19526 psi
@Strain 1.66 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
142.85 MPa
@Strain 1.74 %, Temperature -20.0 °C
|
20719 psi
@Strain 1.74 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
|
157.09 MPa
@Strain 2.33 %, Temperature 0.000 °C
|
22784 psi
@Strain 2.33 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 伸長(zhǎng)率 (斷裂) | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
| 2.6 % | 2.6 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | DAM; ISO 527-1/-2 | |
|
3.213 GPa
@Temperature 150 °C
|
466.0 ksi
@Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
|
3.595 GPa
@Temperature 150 °C
|
521.4 ksi
@Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
|
5.515 GPa
@Temperature 60.0 °C
|
799.9 ksi
@Temperature 140 °F
|
50%RH; ISO 11403-1 -2 | |
|
5.62 GPa
@Temperature 60.0 °C
|
815 ksi
@Temperature 140 °F
|
DAM; ISO 11403-1 -2 | |
|
10.386 GPa
@Temperature -20.0 °C
|
1506.4 ksi
@Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
|
10.498 GPa
@Temperature -20.0 °C
|
1522.6 ksi
@Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 割線模量 |
4.16 GPa
@Strain 2.06 %, Temperature 40.0 °C
|
603 ksi
@Strain 2.06 %, Temperature 104 °F
|
 |
PA66(尼龍66)22G5/長(zhǎng)春化工(漳州)/物性表參數(shù) |
本物性表參數(shù)提供者不承擔(dān)任何法律責(zé)任，建議在選擇材料前，就數(shù)據(jù)值與塑膠材料廠商進(jìn)行驗(yàn)證。版權(quán)歸原作者所有，如有侵權(quán)請(qǐng)立即與我們聯(lián)系.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/臺(tái)化/物性表參數(shù)臺(tái)化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級(jí)合金樹脂，應(yīng)用于筆記型電腦外殼、光碟機(jī)Loader及 Tray盤、螢?zāi)煌鈿ぁ?shù)位相機(jī)外殼、事務(wù)機(jī)器外殼、家用電器外殼、消費(fèi)性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機(jī)械性能，亦同時(shí)具有PC的高沖擊性及耐熱性特質(zhì)，可應(yīng)用於汽車零件、3C電子產(chǎn)品外殼、消費(fèi)性
瀏覽量：12792 -
PC/ABS(PC+ABS合金)AC2300/臺(tái)化/物性表參數(shù)臺(tái)化TAIRILOY PC/ABS AC2300是電鍍級(jí)合金樹脂，應(yīng)用于汽車門把、儀表板、輪圈蓋、汽車零件、消費(fèi)性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機(jī)械性能，亦同時(shí)具有PC的高沖擊性及耐熱性特質(zhì)，可應(yīng)用於汽車零件、3C電子產(chǎn)品外殼、消費(fèi)性電子元件、家電外殼、玩具、板材等產(chǎn)品上，其應(yīng)用端多元化，本廠設(shè)有
瀏覽量：11114 -
TRITAN(美國(guó)伊士曼)TX1001/PCTG(共聚聚酯)物···美國(guó)伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個(gè)基于脫模來源于蔬菜來源。其最突出的特點(diǎn)是優(yōu)良的韌性、水解穩(wěn)定性、耐熱性和耐化
瀏覽量：10763 -
ABS塑料樹脂/PA-757/奇美實(shí)業(yè)/物性表參數(shù)奇美實(shí)業(yè)POLYLAC ABS PA-757 是一般級(jí)高光澤性、超高剛性、特佳彎曲強(qiáng)度的ABS樹脂,熔融指數(shù)是22.g/10min,用途是電視機(jī)前殼、復(fù)印機(jī)外殼 、電話機(jī)殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9142 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉(zhuǎn)換成雙軸取向的薄膜，使用溫度高達(dá)300°F(150°C)，該薄膜具有優(yōu)良的光學(xué)性能、良好的可加工性和優(yōu)良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應(yīng)用的理想產(chǎn)品，其他性能包括阻隔風(fēng)味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數(shù)PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：7936 -
PC(聚碳酸酯)FR6005/科思創(chuàng)(Makrolon)物性表···科思創(chuàng)(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級(jí); 體積熔融指數(shù)MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐沖擊，阻燃等級(jí)，透明高光澤，適用于電子/電氣產(chǎn)品。 以下是PC(聚碳酸
瀏覽量：7905 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強(qiáng)，耐熱級(jí)別的尼龍66原料，拉伸強(qiáng)度在23℃測(cè)試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7331 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數(shù)···寶理塑料(奪鋼)DURACON POM M90-44是一種標(biāo)準(zhǔn)全球品級(jí)型號(hào),高流動(dòng)性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機(jī)械零件方面的應(yīng)用為中心。應(yīng)用在DVD播放器、Blu-ray 光盤播放器等AV機(jī)器；打印機(jī)、復(fù)印機(jī)等OA機(jī)器；洗衣機(jī)、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內(nèi)飾用品等
瀏覽量：6840 -
Bayblend(拜本蘭)FR3010|科思創(chuàng)(PC/ABS合金···科思創(chuàng)Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點(diǎn)溫度/ B 120 = 110C;耐熱性增加;UL認(rèn)可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進(jìn)的化學(xué)抗性和應(yīng)力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6534 -
PA12(尼龍12)TR90|瑞士EMS化學(xué)|物性表參數(shù)科思德塑膠網(wǎng)站提供瑞士EMS化學(xué)PA12 TR90的物性表參數(shù)下載，并且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細(xì)的瑞士EMS化學(xué)PA12(尼龍12)TR90資料以及報(bào)價(jià)。
瀏覽量：6480 -
PP(聚丙烯)HJ730|韓華道達(dá)爾(Hanwha)物性表···韓華道達(dá)爾(Hanwha)高抗沖PP HJ730是與普通均聚PP相比具有高等規(guī)高結(jié)晶度的特點(diǎn)，這一產(chǎn)品的結(jié)晶性能使其具有更好的強(qiáng)度和耐熱性。HJ730非常有助于在電子電器產(chǎn)品和高強(qiáng)度汽車部件上使用，這些部件需要在高溫環(huán)境下長(zhǎng)期暴露.其特點(diǎn)是：高強(qiáng)度、超高耐熱、高結(jié)晶度、良好的表面硬度、良好的色粉分散性。韓華道達(dá)爾PP HJ730物
瀏覽量：6450 -
Makrolon(模克隆)2407(科思創(chuàng))PC(聚碳酸酯)···科思創(chuàng)Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級(jí); 體積熔融指數(shù)19 厘米 3 /10分鐘; 普通用途; 紫外線穩(wěn)定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6344 -
TRITAN(美國(guó)伊士曼)TX1501HF/PCTG(共聚聚酯···美國(guó)伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動(dòng)級(jí)材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對(duì)于伊士曼TRITAN共聚酯TX1001，其他突出的特點(diǎn)包括良好的韌性，水解穩(wěn)定性，耐熱性
瀏覽量：6160 -
PC/ABS(PC+ABS合金)PC-540|奇美實(shí)業(yè)|物性表···奇美實(shí)業(yè)WONDERLOY PC/ABS PC-540是防火級(jí)不含鹵素的難燃PC合金樹脂,熔融指數(shù)是22.g/10min,用途是機(jī)頂盒、投影機(jī)、顯示器前框、3C數(shù)碼產(chǎn)品、變壓器、電視游樂器、小平板計(jì)算機(jī)、網(wǎng)通產(chǎn)品,為了增加PC在薄肉產(chǎn)品的耐沖擊性，可加入ABS樹脂進(jìn)行摻合(blending)，可形成同時(shí)具有高剛性及高耐沖擊性之新材料,一般用于計(jì)算機(jī)外殼及
瀏覽量：6142 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數(shù)嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級(jí)應(yīng)用，在Japan實(shí)現(xiàn)工業(yè)化生產(chǎn)的聚碳酸酯樹脂，長(zhǎng)期以來，帝人一直致力于其性能的提高和
瀏覽量：6041
推薦文章
-
ABS(丙烯腈-丁二烯-苯乙烯共聚物)AG100H|臺(tái)化|物性表參數(shù)
臺(tái)化TAIRILAC ABS AG100H是一種一般級(jí)的丙烯腈-丁二烯-苯乙烯共聚物，性能是超高耐沖擊性、耐低溫沖擊性佳，MI(220℃×10kg): 3、Izod (ASTM,1/4"): 38、FM(ASTM): 19000、TS(ASTM): 370，應(yīng)用于盔帽，鞋跟，管配件，低溫用品。以下是ABS(丙烯腈-丁二烯-苯乙烯共聚物)AG100H|臺(tái)化|物性表參數(shù)物理性能額定值單位制測(cè)試方
-
TPEE/HTR8730/TPEE物性表參數(shù)
TPC-ET 物性TPEE 物性參數(shù)Hytrel HTR8730 BK320 物性表 TPEE HTR8730 BK320是美國(guó)DuPont杜邦公司熱塑性聚酯彈性體TPEE,商品名Hytrel,兼 有橡膠的彈性工程塑料的強(qiáng)度 ,具有優(yōu)異的動(dòng)態(tài)力學(xué)屬性,優(yōu)異的耐
-
PC/ABS（PC合金）NS5000C|LUPOY(LG化學(xué))物性表參數(shù)
LG工程塑料LUPOY PC/ABS NS5000C詳細(xì)介紹 PC/ABS NS5000C是流動(dòng)性高， 廣泛使用汽車內(nèi)部零件，聚碳酸脂具有耐沖擊性、耐熱性。
-
POE(聚烯烴熱塑性彈性體)BL3110M/日本三井/物性表
TAFMER POE BL3110M 是新一代樹脂改良材料，它的出現(xiàn)極大地提高了樹脂材料的性能。作為一種重量輕、易加工的柔性樹脂材料，TAFMER已被廣泛應(yīng)用于汽車配件、包裝材料、體育用品、電線、
-
PC/PET(PC+PET合金)MB4306R|三菱工程塑料|物性表參數(shù)
三菱工程塑料Iupilon PC/PET MB4306R是耐化學(xué)聚碳酸酯/Polyester合金品級(jí),體積熔融指數(shù)25厘米3/10分鐘; 易脫模; 注塑成型,被廣泛地用于各種工業(yè)生產(chǎn)，如運(yùn)動(dòng)器械、汽車部件、光學(xué)儀器、機(jī)械、辦公自動(dòng)化設(shè)備和電子設(shè)備，獲得了客戶的廣泛信賴和支持。Iupilon PC/PET MB4306R物性表參數(shù)PDF文檔下載以下是PC/PET(PC+PET
-
PC(聚碳酸酯)HL-7001|三菱工程塑料|物性表參數(shù)
三菱工程塑料Iupilon/NOVAREX/XANTAR PC HL-7001是高亮度導(dǎo)光品級(jí);超高流動(dòng),體積熔融指數(shù)113厘米3/10分鐘; 易脫模; 注塑成型,三菱工程的聚碳酸酯，在市場(chǎng)上已有好多年歷史, 被廣泛地用于各種工業(yè)生產(chǎn)，如運(yùn)動(dòng)器械、醫(yī)療器械、汽車部件、光學(xué)儀器、機(jī)械、辦公自動(dòng)化設(shè)備和電子設(shè)備，獲得了客戶的廣泛信賴和支持, 三菱工
-
EAA(乙烯-丙烯酸共聚物)5000/埃克森美孚(ExxonMobil)物性表參數(shù)
埃克森美孚(ExxonMobil)Escor EAA 5000主要用于擠出涂覆、共擠涂覆和擠出復(fù)合乙烯-丙烯酸共聚物， 可良好地粘合于極性基材、鋁箔、金屬膜、紙張、鋼鐵和玻璃表面，提供與基材表面的粘合性和與共擠的低密度聚乙烯和乙烯醋酸乙烯酯的層間結(jié)合力的出色平衡， 薄膜中有很好的粘合性聚合體。以下是EAA(乙烯-丙烯酸共聚物)5000/埃
-
PA66(尼龍66)91G40|Leona(尼胺龍)|旭化成|物性表參數(shù)
旭化成Leona(尼胺龍)PA66 91G40是一種表面平滑，低翹曲性。玻璃纖維和礦物填充的尼龍66材料，比重是1.46g/cm3，應(yīng)用于汽車外部零件。以下是PA66(尼龍66)91G40/Leona(尼胺龍)/旭化成/物性表參數(shù)物理性能干燥調(diào)節(jié)后的單位制測(cè)試方法比重1.46--g/cm3ASTM D792,
-
PP(聚丙烯聚合物)J-560S/樂天化學(xué)/物性表參數(shù)
樂天化學(xué)(LOTTE CHEMICAL)PP J-560S是一種注塑級(jí)聚丙烯聚合物，比重(23°C)是0.9克/厘米3，熔體流動(dòng)速率(230°C/2.16kg)是18克/10分鐘，該牌號(hào)設(shè)計(jì)用于在常規(guī)注塑設(shè)備中加工，具有超優(yōu)異的透明度，良好的剛度/沖擊強(qiáng)度平衡，高光澤，高鉸鏈性能和低氣味，用于化妝品容器與蓋、食品容器、透明外殼、文具類、CD / DVD盒。
-
PMMA(亞克力)ZK5HF/贏創(chuàng)德固賽/物性表參數(shù)
贏創(chuàng)德固賽(PLEXIGLAS)Resist PMMA ZK5HF是一種沖擊改性的熱塑性PMMA(亞克力)丙烯酸基多聚物，工藝是型材擠出成型和注塑成型，典型性能是：高強(qiáng)度、優(yōu)良的耐候性、抗沖擊強(qiáng)度好、良好的透光性、表面硬度高，耐磨損、良好的著色性、耐氣候影響性能良好、提高抗應(yīng)力開裂能力，適用于鑄模/模具/工具、墻板、片材、紡織應(yīng)用。