PPO(聚苯醚)|NORYL|PX9406K/沙伯基礎/物性表參數

日期：2020-11-06 03:14:05 編輯：科思德塑膠來源：科思德塑膠瀏覽：462

沙伯基礎(SABIC)NORYL PPO PX9406K是一種阻燃聚苯醚(PPO) ，適用于消費電子產品的應用，使用的阻燃劑是無鹵化的，UL94 V0在1.5 mm, 5VB在2 mm, 5VA在2.5 mm。RTI(impact)= 105°。

以下是PPO(聚苯醚)PX9406K/沙伯基礎(NORYL)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E207780-101401128	-	-
UL Recognized, 94V-0 Flame Class Rating		≥1.5	mm	UL 94
UL Recognized, 94-5VA Flame Class Rating		≥2.5	mm	UL 94
UL Recognized, 94-5VB Flame Class Rating		≥2	mm	UL 94
Glow Wire Flammability Index, 1.5 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 2.0 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm		960	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.5 mm		800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm		800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm		800	°C	IEC 60695-2-13
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min		66	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min		50	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min		5.7	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min		45	%	ASTM D 638
Tensile Modulus, 50 mm/min		2700	MPa	ASTM D 638
Flexural Stress, yield, 6.4 mm		101	MPa	ASTM D 790
Flexural Stress, yld, 1.3 mm/min, 50 mm span		100	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span		2650	MPa	ASTM D 790
Flexural Modulus, 6.4 mm		2650	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min		67	MPa	ISO 527
Tensile Stress, break, 50 mm/min		52	MPa	ISO 527
Tensile Strain, yield, 50 mm/min		5	%	ISO 527
Tensile Strain, break, 50 mm/min		55	%	ISO 527
Tensile Modulus, 1 mm/min		2550	MPa	ISO 527
Flexural Stress, yield, 2 mm/min		104	MPa	ISO 178
Flexural Modulus, 2 mm/min		2420	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C		170	J/m	ASTM D 256
Izod Impact, notched, -30°C		100	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C		55	J	ASTM D 3763
Izod Impact, notched 80104 +23°C		12	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C		5	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm		13	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm		5	kJ/m²	ISO 179/1eA
THERMAL
HDT, 0.45 MPa, 3.2 mm, unannealed		128	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed		113	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed		130	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed		121	°C	ASTM D 648
Ball Pressure Test, 125°C +/- 2°C		PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/120		144	°C	ISO 306
Vicat Softening Temp, Rate B/120		134	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		111	°C	ISO 75/Af
Relative Temp Index, Elec	¹⁾	110	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	110	°C	UL 746B
PHYSICAL
Specific Gravity		1.1	-	ASTM D 792
Density		1.1	g/cm³	ISO 1183
Melt Volume Rate, MVR at 250°C/10.0 kg		7	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 280°C/5.0 kg		11	cm³/10 min	ISO 1133
Melt Viscosity, 250°C, 1500 sec-1		525	Pa-s	ISO 11443
Melt Viscosity, 260°C, 1500 sec-1		390	Pa-s	ISO 11443
Melt Viscosity, 280°C, 1500 sec-1		250	Pa-s	ISO 11443
ELECTRICAL
Volume Resistivity		1.4E+17	Ohm-cm	ASTM D 257
Dielectric Strength, in air, 3.2 mm		49	kV/mm	ASTM D 149
High Voltage Arc Track Rate {PLC}		3	PLC Code	UL 746A
Comparative Tracking Index	²⁾	250	V	IEC 60112
Comparative Tracking Index (UL) {PLC}		2	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 0		≥1.5	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥1.5	mm	UL 746A
Arc Resistance, Tungsten {PLC}		6	PLC Code	ASTM D 495
Injection Molding
Drying Temperature		105-110	°C
Drying Time		3-4	hrs
Drying Time (Cumulative)		8	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		275-305	°C
Nozzle Temperature		275-305	°C
Front - Zone 3 Temperature		265-305	°C
Middle - Zone 2 Temperature		255-300	°C
Rear - Zone 1 Temperature		245-295	°C
Mold Temperature		70-100	°C
Back Pressure		0.3-0.7	MPa
Screw Speed		20-100	rpm
Shot to Cylinder Size		30-70	%
Vent Depth		0.038-0.051	mm