Acrypet三菱麗陽PMMA VRS40物性表數(shù)據(jù)（中英文版）
Acrypet三菱麗陽PMMA VRS40物性特性用途
|
MITSUBISHI RAYON Acrypet® VRS40 PMMA
|
||
|
特性用途：高抗沖擊性、高流動性，可用于汽車、家電、光學(xué)部件。
|
||
|
備注：000是不含紫外線吸收劑，001是含紫外線吸收劑，002顏色是藍(lán)底。
|
||
|
Physical Properties物理性質(zhì)
|
Metric公制數(shù)據(jù)
|
Comments測試方法
|
|
Specific Gravity密度
|
1.16 g/cc
|
JIS K7112;ISO 1183
|
|
Water Absorption吸水率
|
0.3 %
|
24 hours; JIS K7209; ISO 62
|
|
Mold Shrinkage成型收縮率
|
0.3-0.7%
|
MRC Method
|
|
Melt Index of Compound熔體流動速率
|
7.7 g/10 min
230℃,37.3N |
JIS K7210；ISO 1133
|
|
Mechanical Properties力學(xué)性能
|
Metric公制數(shù)據(jù)
|
Comments測試方法
|
|
M scale洛式硬度M
|
59
|
JIS K7202；ISO 2039
|
|
Tensile Strength at Break抗拉強(qiáng)度
|
47.0 MPa
|
JIS K7162; ISO 527
|
|
Elongation at Break斷裂伸長率
|
15 %
|
JIS K7162; ISO 527
|
|
Flexural Strength抗彎強(qiáng)度
|
69.0 MPa
|
JIS K7171; ISO 178
|
|
Flexural Modulus彎曲彈性模量
|
1.9 GPa
|
JIS K7162; ISO 527
|
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度
|
8.20 kJ/m2
|
JIS K7111; ISO 179
|
|
Electrical Properties電性能
|
Metric公制數(shù)據(jù)
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
>1013Ωm
|
JIS K6911
|
|
Dielectric Constant介電常數(shù)
|
3.7
@Frequency 60 Hz |
JIS K6911
|
|
Dielectric Strength絕緣擊穿強(qiáng)度
|
20.0 MV/m
|
4kV/s; JIS K6911
|
|
Dissipation Factor介質(zhì)衰耗因數(shù)
|
0.05
@Frequency 60 Hz |
JIS K6911
|
|
Thermal Properties熱性能
|
Metric公制數(shù)據(jù)
|
Comments測試方法
|
|
CTE, linear線性膨脹系數(shù)
|
9×10-5 1/℃
|
JIS K7197
|
|
Deflection Temperature at載荷撓曲溫度1.8 MPa (264 psi)
|
81.0 °C
|
JIS K7191；ISO 75
|
|
Vicat Softening Point維卡軟化點(diǎn)
|
87 °C
|
B50; JIS K7206；ISO 306
|
|
Annealing Point退火點(diǎn)(空氣浴)
|
65.0 - 75.0 °C
|
1-3 hours
|
|
Flammability, UL94阻燃等級(1.5mm,3.0mm)
|
HB
|
File No.E256044
|
|
Optical Properties光學(xué)性質(zhì)
|
Metric公制數(shù)據(jù)
|
Comments測試方法
|
|
ReFRactive Index折射率
|
1.49
|
JIS K7142/ISO 489
|
|
Haze霧度
|
0.7 %
@Thickness 3.00 mm |
JIS K7136/ISO 14782
|
|
TRansmission, Visible光線透射率
|
92 %
@Thickness 3.00 mm |
JIS K7361/ISO 13468
|
|
Processing Properties加工性能
|
Metric公制數(shù)據(jù)
|
Comments測試方法
|
|
Processing Temperature加工溫度
|
200 - 260 °C
|
Injection molding cylinder temperature
|
|
Mold Temperature模具溫度
|
40 - 80 °C
|
|
|
Drying Temperature干燥溫度
|
70.0 - 80.0 °C
|
|
|
Dry Time干燥時(shí)間
|
4 - 6 hour
|
|
|
Injection Pressure注射壓力
|
70- 150 MPa
|
|
Acrypet三菱麗陽PMMA VRS40物性特性用途
PMMA VRS40特性用途：高抗沖擊性、高流動性，可用于汽車、家電、光學(xué)部件。
PMMA VRS40原產(chǎn)地及生產(chǎn)廠商：三菱麗陽高分子材料（南通）有限公司/日本三菱麗陽株式會社MITSUBISHI RAYON CO.,LTD.
PMMA VRS40產(chǎn)品發(fā)生裂紋、龜裂的原因及解決辦法
這是發(fā)生在產(chǎn)品表面或與嵌入物接觸面的龜裂現(xiàn)象、從某個(gè)角度觀察會閃爍發(fā)光。導(dǎo)致這一現(xiàn)象發(fā)生的原因比較復(fù)雜、可通過以下方法防止其發(fā)生：
1，提高料筒溫度
2，提高模具溫度
3，提高注塑速度
4，調(diào)節(jié)注塑壓力